Microstructural study of a conducting polymer doped with carbon nanotubes
dc.contributor.author | Söderberg, Fredik | |
dc.contributor.department | Chalmers tekniska högskola / Institutionen för fysik | sv |
dc.contributor.examiner | Olsson, Eva | |
dc.contributor.supervisor | Olsson, Eva | |
dc.date.accessioned | 2021-11-18T07:58:21Z | |
dc.date.available | 2021-11-18T07:58:21Z | |
dc.date.issued | 2021 | sv |
dc.date.submitted | 2020 | |
dc.description.abstract | This work concerns the microsctructure of benzimidazobenzophenanthroline, BBL, films doped with carbon nanotubes, CNTs, to increase the electron mobility of the films. The CNT dopings were 1, 9 and 50 wt% respectively. The microsctructures were studied using electron microscopy including scanning electron microscopy and transmission electron microscopy. The morphology of the films gradually changed from a continuous BBL film with a relatively rough surface morphology in the 1 wt% films with randomly oriented CNTs to a structure with the BBL forming a smooth shell of BBL on the CNTs. The CNTs were multiwalled with a high density of defects. The thickness of the BBL shell was about 20-30 nm in the 1 and 9 wt% films and 3-4 nm in the 50 wt% films. The results show that the electron mobility can be even further increased by aligning the CNTs that have a considerably higher mobility along their long axis and also compared to the BBL. It should be noted that an alignment of the CNTs would also result in a high directional anisotropy of the mobility in the BBL:CNT films. | sv |
dc.identifier.coursecode | TIFX05 | sv |
dc.identifier.uri | https://hdl.handle.net/20.500.12380/304366 | |
dc.language.iso | eng | sv |
dc.setspec.uppsok | PhysicsChemistryMaths | |
dc.subject | BBL | sv |
dc.subject | CNT | sv |
dc.subject | SEM | sv |
dc.subject | STEM | sv |
dc.subject | TEM | sv |
dc.subject | SE | sv |
dc.subject | doped polymer films | sv |
dc.subject | microsctructure | sv |
dc.title | Microstructural study of a conducting polymer doped with carbon nanotubes | sv |
dc.type.degree | Examensarbete för masterexamen | sv |
dc.type.uppsok | H |