Titanium Aluminide Manufactured by Electron Beam Melting

Examensarbete för masterexamen

Please use this identifier to cite or link to this item: https://hdl.handle.net/20.500.12380/127716
Download file(s):
File Description SizeFormat 
127716.pdfFulltext7.19 MBAdobe PDFView/Open
Type: Examensarbete för masterexamen
Master Thesis
Title: Titanium Aluminide Manufactured by Electron Beam Melting
Authors: Fager Franzén, Sanna
Karlsson, Joakim
Abstract: Gamma titanium aluminides (γ-TiAl) have been recognized for decades to be suitable for aerospace applications due to their low density and high strength at elevated temperatures. However, TiAl is limited in application due to difficulties during machining which arise from the inherent brittle nature associated with intermetallic phases. Electron Beam Melting (EBM) has recently been proven as a processing method to produce complex, near net shape γ-TiAl parts with short lead times. In this report the resulting microstructure from the as-EBM built material is presented. The as-EBM-built material is treated through Hot Isostatic Pressing (HIP) and thoroughly investigated using optical microscope, SEM and FIB-SEM technologies. From the as-HIPed material different heat treatments were applied to achieve the theoretical available microstructures. The heat treated material was evaluated using SEM and grain size measurements. By using tensile testing the mechanical properties of all different treatments were evaluated. The results from investigations conclude that EBM is a feasible way to produce γ-TiAl material. Different microstructures are achievable with applicable heat treatments and process parameters from the EBM machine. By using the EBM technology γ-TiAl produced material will experience unique microstructural features with very small grain size.
Keywords: Materialvetenskap;Materialteknik;Konstruktionsmaterial;Materials Science;Materials Engineering;Construction materials
Issue Date: 2010
Publisher: Chalmers tekniska högskola / Institutionen för material- och tillverkningsteknik
Chalmers University of Technology / Department of Materials and Manufacturing Technology
Series/Report no.: Diploma work - Department of Materials and Manufacturing Technology, Chalmers University of Technology : 37
URI: https://hdl.handle.net/20.500.12380/127716
Collection:Examensarbeten för masterexamen // Master Theses (IMS)

Items in DSpace are protected by copyright, with all rights reserved, unless otherwise indicated.