THE EFFECT OF NI ON THE SECONDARY CORROSION PROTECTION OF FE BASED MODEL ALLOYS AT 600 °C

Visa enkel post
dc.contributor.authorLaurell, Carl
dc.contributor.departmentChalmers tekniska högskola / Institutionen för kemi och kemitekniksv
dc.contributor.departmentChalmers University of Technology / Department of Chemistry and Chemical Engineeringen
dc.date.accessioned2019-07-03T14:58:55Z
dc.date.available2019-07-03T14:58:55Z
dc.date.issued2018
dc.description.abstractThe formation of secondary protective oxides has been investigated for three different alloys with different wt% nickel. The presence of alkali salts causing severe corrosion of stainless steel in biomass- and waste- fired boilers. All the alloys showed a breakdown of the primary protective oxide scale after exposure to K2CO3 and KCl for 24 hours at 600°C. The samples were sprayed with 1 mg/cm2 of saturated alkali salts before being placed in the furnace. An increased amount of nickel resulted in an increased formation of nickel oxide (NiO) and a decreased formation of iron oxide (Fe2O3). The increase in formation of nickel oxide showed a connection to lower mass gain for all the samples exposed to alkali salts. The nickel oxide was shown to grow slower than the iron oxide and had better protective properties. The alloy containing 34 wt% nickel was specifically targeted by water containing environment.
dc.identifier.urihttps://hdl.handle.net/20.500.12380/256498
dc.language.isoeng
dc.setspec.uppsokPhysicsChemistryMaths
dc.subjectKemi
dc.subjectKemiteknik
dc.subjectChemical Sciences
dc.subjectChemical Engineering
dc.titleTHE EFFECT OF NI ON THE SECONDARY CORROSION PROTECTION OF FE BASED MODEL ALLOYS AT 600 °C
dc.type.degreeExamensarbete på grundnivåsv
dc.type.uppsokM
local.programmeKemiteknik 180 hp (högskoleingenjör)
Ladda ner
Original bundle
Visar 1 - 1 av 1
Bild (thumbnail)
Namn:
256498.pdf
Storlek:
2.53 MB
Format:
Adobe Portable Document Format
Beskrivning:
Fulltext
Ladda ner
Samling
Examensarbeten på grundnivå